    What is the correct metal finish for seat rails?

    I just cleaned up seat rails and I beleive should have some protective coating. Are they anadized?

    Name:  911 seat rails smaller.jpg
Views: 372
Size:  34.6 KB
    Haasman

    Registry #2489
    R Gruppe #722
    65 911 #302580
    70 914-6 #9140431874
    73 911s #9113300709

  2. #2
    Mark Smedley says those are among the few parts that are actually still cad plated.
    Early S Registry member #90
    R Gruppe member #138
    Fort Worth Tx.

  3. #3
    Ed -

    Is there a time period where the cad stopped being used? The ones on my '73 sure look like zinc to me!

    - Rob

  4. #4
    Back in the early 70s I had the rails from my '70T analyzed by two platers and a metallurgist for Champion Spark Plug who just happened to be a PCA member and concours guy.....definately silver cadmium. Multiple restoration projects up through '73 cars...all silver cadmium. Always curious why cadmium....my metallurgist pal suggested that cadmium is softer and created less friction....they were sliders! Subsequent SWB projects and research also confirm cadmium.
    Mark Smedley
    '59 VW Typ I
    '69 911T 2.7
    '86 930
    '04 GT3
    '16 Boxster GTS
    '08 MBZ AMG CLK 63 Black Series

  5. #5
    The ones in my '65 coupe were silver zinc. Not an opinion but verified through a plating testing kit given to me by Tim Goodrich years back

  6. #6
    Quote Originally Posted by 718RSK View Post
    The ones in my '65 coupe were silver zinc. Not an opinion but verified through a plating testing kit given to me by Tim Goodrich years back
    Could be. Tim and I had discussed this. My unrestored '64 C had zinc rails. The industry
    was changing in the late 60s. Fasteners went from clear to yellow zinc...rails changed as well.
    Mark Smedley
    '59 VW Typ I
    '69 911T 2.7
    '86 930
    '04 GT3
    '16 Boxster GTS
    '08 MBZ AMG CLK 63 Black Series

  7. #7
    Senior Member Haasman's Avatar
    Join Date
    Apr 2011
    Location
    N.Calif., south of SF
    Posts
    1,965
    So these are for my late '65, '66 model year 911.

    silver zinc or cadium?
    Haasman

    Registry #2489
    R Gruppe #722
    65 911 #302580
    70 914-6 #9140431874
    73 911s #9113300709

  8. #8
    The actual build date would only be partially helpful as this is a supplier issue...not a factory specification.
    An educated guess would be to survey the original fasteners in the car. These cars were being built with fasteners who's industry was changing it's specifications, not only actual DIN dimensions but plating.
    If your car was built with predominantly clear (silver) zinc fasteners, go with silver zinc. If you have a lot of later yellow zinc fasteners, go with cadmium on the rails.

    The other issue is that the current zinc plating process results in zinc that is a bright bluish finish...far different from the older dull silver of the original pre-EPA process. If you went with "new zinc" you'd have top knock it down a bit to flatten it.

    In the old days silver zinc and silver cadmium were VERY similar when fresh..thus the confusion. One way to differentiate is old zinc dulls and blackens with break through ferrous oxide. Old cadmium chalks with a white powdery residue and break through rust.
    Mark Smedley
    '59 VW Typ I
    '69 911T 2.7
    '86 930
    '04 GT3
    '16 Boxster GTS
    '08 MBZ AMG CLK 63 Black Series

  9. #9
    Senior Member Haasman's Avatar
    Join Date
    Apr 2011
    Location
    N.Calif., south of SF
    Posts
    1,965
    Thanks Mark. Very helpful. These are for #302580 with a build date of 11-2-65. The allen screws are silver color, not yellow.
    Haasman

    Registry #2489
    R Gruppe #722
    65 911 #302580
    70 914-6 #9140431874
    73 911s #9113300709

  10. #10
    The blue finish on zinc plating is a chromate that is similar to yellow chromate. The chromate is a protective coating to help prevent oxidation of the raw zinc. Zinc plating is silver when it comes out of the bath until chromated or left as-plated.

    I am sure you could direct your zinc plating provider to leave parts "raw".
    Paul Abbott
    Early S Member #18
    Weber service specialist
    www.PerformanceOriented.com
    info@PerformanceOriented.com
    530.520.5816

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •  

Message Board Disclaimer and Terms of Use
This is a public forum. Messages posted here can be viewed by the public. The Early 911S Registry is not responsible for messages posted in its online forums, and any message will express the views of the author and not the Early 911S Registry. Use of online forums shall constitute the agreement of the user not to post anything of religious or political content, false and defamatory, inaccurate, abusive, vulgar, hateful, harassing, obscene, profane, sexually oriented, threatening, invasive of a person's privacy, or otherwise to violate the law and the further agreement of the user to be solely responsible for and hold the Early 911S Registry harmless in the event of any claim based on their message. Any viewer who finds a message objectionable should contact us immediately by email. The Early 911S Registry has the ability to remove objectionable messages and we will make every effort to do so, within a reasonable time frame, if we determine that removal is necessary.